Volumic Mass |
2,65 grs/cm3 |
Absorption Coefficient |
0,15 % |
Porosity |
0,40 % |
Knoop Microhardness |
155 kg/mm2 |
Variation of Bending Modulus |
0,10 % |
Mechanical Resistance to Compression |
1266 kg/cm2 |
Mechanical Resistance to Bending |
118,5 kg/cm2 |
Resistance to Wear |
8,43 mm |
Impact Resistance |
23,3 cm |
Constructions
Volumic Mass |
2,65 grs/cm3 |
Absorption Coefficient |
0,15 % |
Porosity |
0,40 % |
Knoop Microhardness |
155 kg/mm2 |
Variation of Bending Modulus |
0,10 % |
Mechanical Resistance to Compression |
1266 kg/cm2 |
Mechanical Resistance to Bending |
118,5 kg/cm2 |
Resistance to Wear |
8,43 mm |
Impact Resistance |
23,3 cm |
Constructions
Volumic Mass |
- |
Absorption Coefficient |
- |
Porosity |
- |
Knoop Microhardness |
- |
Variation of Bending Modulus |
- |
Mechanical Resistance to Compression |
- |
Mechanical Resistance to Bending |
- |
Resistance to Wear |
- |
Impact Resistance |
- |
Constructions
Volumic Mass |
2,65 grs/cm3 |
Absorption Coefficient |
0,15 % |
Porosity |
0,40 % |
Knoop Microhardness |
155 kg/mm2 |
Variation of Bending Modulus |
0,10 % |
Mechanical Resistance to Compression |
1266 kg/cm2 |
Mechanical Resistance to Bending |
118,5 kg/cm2 |
Resistance to Wear |
8,43 mm |
Impact Resistance |
23,3 cm |
Constructions
Volumic Mass |
2,65 grs/cm3 |
Absorption Coefficient |
0,15 % |
Porosity |
0,40 % |
Knoop Microhardness |
155 kg/mm2 |
Variation of Bending Modulus |
0,10 % |
Mechanical Resistance to Compression |
1266 kg/cm2 |
Mechanical Resistance to Bending |
118,5 kg/cm2 |
Resistance to Wear |
8,43 mm |
Impact Resistance |
23,3 cm |
Constructions
Volumic Mass |
2,65 grs/cm3 |
Absorption Coefficient |
0,15 % |
Porosity |
0,40 % |
Knoop Microhardness |
155 kg/mm2 |
Variation of Bending Modulus |
0,10 % |
Mechanical Resistance to Compression |
1266 kg/cm2 |
Mechanical Resistance to Bending |
118,5 kg/cm2 |
Resistance to Wear |
8,43 mm |
Impact Resistance |
23,3 cm |
Constructions